Physical Properties: Plexiglass G Sheet

ePlastics

by

4/10/2018 2:48 pm

TYPICAL PHYSICAL PROPERTIES: .118" & .220" PLEXIGLAS® G CLEAR SHEET

LINKS:

Plexiglass Acrylic Sheets
LuciteLux®
Material Guide
Cutting/Finishing Capabilities & Rates
Custom Fabrication


PROPERTY
ASTM METHOD
UNITS
Plexiglas® G
MISCELLANEOUS
Thickness, measured
.

in

0.118"
Specific gravity
D792
-
1.18
Rockwell Hardness (M-scale)
D785
-
100
OPTICAL
Refractive index
Light transmittance
Haze
.
D542
D1003

-
%
%

1.49
92
<2
MECHANICAL
Tensile Properties
Maximum
Rupture
Modulus of elasticity


D638


psi
psi
psi


10,500
10,500
450,000
Flexural Properties (span depth
ratio 16, 0.1 in/min)
Maximum
Modulus of elasticity

D790


psi
psi


16,000
400,000
Impact Properties
Izod milled notch @ 73°F

D256

ft-lb/in of notch

0.27
THERMAL
Deflection temperature under
(flexural) load
3.6° F/min-264 psi


D648



°F



200
Maximum Recommended Continuous Service Temperature
°F
180-200
ELECTRICAL
Dielectric strength, short time test
D149
volts/mil
500

The statements, technical information and recommendations obtained herein are believed to be accurate as of the date hereof. Since the conditions and methods of use of the product and of the information referred to herein are beyond our control, Arkema expressly disclaims any and all liability. NO WARRANTY OF FITNESS FOR ANY PARTICULAR PURPOSE, WARRANTY OR MERCHANTABILITY, OR ANY OTHER WARRANTY, EXPRESS OR IMPLIED, IS MADE CONCERNING THE GOODS DESCRIBED OR THE INFORMATION PROVIDED HEREIN. The information provided herein relates only to the specific product designated and may not be applicable when such product is used in combination with other materials or in any process. The user should thoroughly test any application before commercialization. Nothing contained herein should be construed as an inducement to infringe any patent, and the user is advised to take appropriate steps to be sure that any proposed use of the product will not result in patent infringement.